FR4 classification

The surface color of FR-4 epoxy glass cloth laminate is as follows:
Yellow FR-4, white FR-4, black FR-4, blue FR-4, etc.
FR-4 is the base plate used by PCB, and it is a kind of sheet metal. According to the different reinforcing materials, sheets are mainly classified into the following four types:
1) FR-4: Glass Cloth Substrate
2) FR-1, FR-2, etc.: Paper Substrate
3) CEM Series: Composite Substrate
4) FR-4 of special material substrates (ceramics, metal substrates, etc.) is a plate-like laminated product made of epoxy phenolic resin and other materials impregnated with special electronic cloth by hot pressing at high temperature and pressure.
Features: It has high mechanical and dielectric properties, good heat and moisture resistance and good machinability.
Usage: Used as insulating structural parts in motor and electrical equipment, including various types of switch FPC reinforcing electrical insulation carbon film printed circuit board, computer drilling cushion die fixture (PCB test stand), and can be used in humid environment and transformer oil.
ENERGETIC Established in 2008, a professional One-stop manufacturer of Semi-finished Plastics & Metals, plastic extrusion profiles
  • – General Plastic
  • – Engineering Plastic
  • – Thermosetting Plastic
  • – ESD/Anti-static Plastic & Material
  • – Metal material
Further services for Customized Precision Mechanical Parts
  • – Cut into required sizes
  • – CNC Machined Metal Parts
  • – CNC Machined Plastic Parts
  • – SMT Jigs, PCB Testing Fixtures

评论

发表评论

此博客中的热门博文

How to deal with the problem of fusion line?

图片
Reason analysis: From the perspective of plastics, the melting line is essentially caused by the incomplete melting of two plastic flow fronts. Solution: To eliminate or reduce the melting line, plastics must have low viscosity, high temperature, sufficient pressure and enough time to melt completely. Usually, in the case of good exhaust, accelerating the filling and feeding speed and increasing the pressure as soon as possible after the combination of two plastic flow fronts will help to solve the melting line problem.
阅读全文

How to solve the problem of surface depression?

图片
Basic Reasons : From the perspective of plastics, when the plastics are cooled and contracted, insufficient feeding will lead to dents on the external surface or holes in the interior of the products. Depression occurs in different locations, and the causes and solutions of the defects are also different. 1. When the depression occurs at the final cooling position of the thick-walled product or at a distance from the gate: Cause analysis: Typical surface depressions or voids at the thick wall and far away from the gate are usually due to the increase of effective viscosity and pressure loss, resulting in insufficient cavity pressure, resulting in insufficient feeding pressure. Solution: Increase the pressure of feeding and speed up the feeding rate 2. Surface depressions or cavitations occur near the gate Cause analysis: Depression occurs near gate, usually due to lack of gate freezing. There are several reasons affecting gate freezing: it may be caused by the decrease of ef...
阅读全文

Analysis of Common Defects in Plastic Products-Size Change

Basic Reasons: From the perspective of plastics, the reasons for the size change are as follows: The change of pressure distribution in U-shaped cavity will cause the change of size. For crystalline plastics, the change of crystallinity due to the change of cooling rate will cause the change of size. After-treatment of U products, changes in ambient temperature and humidity can also cause size changes. Next, the change of pressure distribution in the cavity and the size change are analyzed and discussed. The causes of defects will vary with the size changes. First, defect phenomenon: the overall product size is too small. Cause analysis: the plastic pressure in the cavity is too low. Solution: Increase the feeding pressure to meet the cavity pressure required by qualified products. 2. Defects: Overall product size is too large Cause analysis: the plastic pressure in the cavity is too high. Solution: Reduce the feeding pressure to achieve the cavity pressure require...
阅读全文