Detailed Explanation of Material Characteristics of PTFE Plate

Polytetrafluoroethylene sheet is made of 100% pure polytetrafluoroethylene by moulding, turning, cutting and other processes.

Among the known plastics, it has the best chemical corrosion resistance, no aging, electrical insulation, and very low friction coefficient. It can be used at - 180 ~ + 260 degrees without load.

Characteristic, high temperature resistance - working temperature up to 250 C.

Polytetrafluoroethylene (PTFE) sheet has good mechanical toughness and low temperature resistance, and can maintain 5% elongation even when the temperature drops to - 196 (?)

Polytetrafluoroethylene (PTFE) sheets are corrosion resistant - inert to most chemicals and solvents, strong acid and alkali, water and various organic solvents.

Polytetrafluoroethylene (PTFE) boards are climate-resistant and have the best aging life of plastics. High lubrication - the lowest coefficient of friction in solid materials.

Non-adherence - is the smallest surface tension in solid materials. It does not adhere to any substance. Its mechanical properties have very small friction coefficient, which is only 1/5 of polyethylene. This is an important feature of perfluorocarbon surface. Because the interaction force between fluorine and carbon chain is very low, PTFE is not viscous.

Non-toxic - physiological inertia, as artificial blood vessels and organs long-term implantation in vivo without adverse reactions.

评论

发表评论

此博客中的热门博文

How to deal with the problem of fusion line?

图片
Reason analysis: From the perspective of plastics, the melting line is essentially caused by the incomplete melting of two plastic flow fronts. Solution: To eliminate or reduce the melting line, plastics must have low viscosity, high temperature, sufficient pressure and enough time to melt completely. Usually, in the case of good exhaust, accelerating the filling and feeding speed and increasing the pressure as soon as possible after the combination of two plastic flow fronts will help to solve the melting line problem.
阅读全文

How to solve the problem of surface depression?

图片
Basic Reasons : From the perspective of plastics, when the plastics are cooled and contracted, insufficient feeding will lead to dents on the external surface or holes in the interior of the products. Depression occurs in different locations, and the causes and solutions of the defects are also different. 1. When the depression occurs at the final cooling position of the thick-walled product or at a distance from the gate: Cause analysis: Typical surface depressions or voids at the thick wall and far away from the gate are usually due to the increase of effective viscosity and pressure loss, resulting in insufficient cavity pressure, resulting in insufficient feeding pressure. Solution: Increase the pressure of feeding and speed up the feeding rate 2. Surface depressions or cavitations occur near the gate Cause analysis: Depression occurs near gate, usually due to lack of gate freezing. There are several reasons affecting gate freezing: it may be caused by the decrease of ef...
阅读全文

Analysis of Common Defects in Plastic Products-Size Change

Basic Reasons: From the perspective of plastics, the reasons for the size change are as follows: The change of pressure distribution in U-shaped cavity will cause the change of size. For crystalline plastics, the change of crystallinity due to the change of cooling rate will cause the change of size. After-treatment of U products, changes in ambient temperature and humidity can also cause size changes. Next, the change of pressure distribution in the cavity and the size change are analyzed and discussed. The causes of defects will vary with the size changes. First, defect phenomenon: the overall product size is too small. Cause analysis: the plastic pressure in the cavity is too low. Solution: Increase the feeding pressure to meet the cavity pressure required by qualified products. 2. Defects: Overall product size is too large Cause analysis: the plastic pressure in the cavity is too high. Solution: Reduce the feeding pressure to achieve the cavity pressure require...
阅读全文