UHMWPE Plastic rollers features


UHMWPE rollers are made from ultra-high molecular weight polyethylene sheet/UHMW sheet or UHMWPE rod and retained properties of ultra-high molecular polyethylene.

The wear resistance of UHMWPE is 7 times than steel and 3 times than nylon.
The surface hardness of UHMWPE roller is low, the friction coefficient is small, the self lubrication performance is high, and the wear of the belt will not be caused.

Rain, ice and snow, acid, alkali liquid spatter will not be corroded.

Because of light weight, the installation and replacement of UHMWPE roller is easy and convenient.

The working environment is purified because of its rotation without noise.

And it’s able to withstand repeated shocks and vibrations.

ENERGETIC industry, the plastic fabrication company’s UHMWPE plastic rollers after years of use, the results show that the UHMWPE roller operation is in 25000 h-35000 H, with characteristic of flexible rotation, small resistance, it always give no damage to your belt, convenient for you to installation, free for you to maintenance. Which shall save you a lot of manpower and electricity, so as to bring the considerable economic benefits to you in the use process.

You can use UHMWPE roller in the open air even dust is large, high corrosive environment, such as mines, power plants, steel mills, stone factory, cement factory and coking plant, coal washing, salt, soda plant, fertilizer plant, transportation terminals and other places.

评论

发表评论

此博客中的热门博文

How to deal with the problem of fusion line?

图片
Reason analysis: From the perspective of plastics, the melting line is essentially caused by the incomplete melting of two plastic flow fronts. Solution: To eliminate or reduce the melting line, plastics must have low viscosity, high temperature, sufficient pressure and enough time to melt completely. Usually, in the case of good exhaust, accelerating the filling and feeding speed and increasing the pressure as soon as possible after the combination of two plastic flow fronts will help to solve the melting line problem.
阅读全文

How to solve the problem of surface depression?

图片
Basic Reasons : From the perspective of plastics, when the plastics are cooled and contracted, insufficient feeding will lead to dents on the external surface or holes in the interior of the products. Depression occurs in different locations, and the causes and solutions of the defects are also different. 1. When the depression occurs at the final cooling position of the thick-walled product or at a distance from the gate: Cause analysis: Typical surface depressions or voids at the thick wall and far away from the gate are usually due to the increase of effective viscosity and pressure loss, resulting in insufficient cavity pressure, resulting in insufficient feeding pressure. Solution: Increase the pressure of feeding and speed up the feeding rate 2. Surface depressions or cavitations occur near the gate Cause analysis: Depression occurs near gate, usually due to lack of gate freezing. There are several reasons affecting gate freezing: it may be caused by the decrease of ef...
阅读全文

Analysis of Common Defects in Plastic Products-Size Change

Basic Reasons: From the perspective of plastics, the reasons for the size change are as follows: The change of pressure distribution in U-shaped cavity will cause the change of size. For crystalline plastics, the change of crystallinity due to the change of cooling rate will cause the change of size. After-treatment of U products, changes in ambient temperature and humidity can also cause size changes. Next, the change of pressure distribution in the cavity and the size change are analyzed and discussed. The causes of defects will vary with the size changes. First, defect phenomenon: the overall product size is too small. Cause analysis: the plastic pressure in the cavity is too low. Solution: Increase the feeding pressure to meet the cavity pressure required by qualified products. 2. Defects: Overall product size is too large Cause analysis: the plastic pressure in the cavity is too high. Solution: Reduce the feeding pressure to achieve the cavity pressure require...
阅读全文